TS 33
Suitable for
-
Wave soldering is a bulk soldering process used in electronics manufacturing to connect electronic components to a PCB board. The process is typically used for through hole components but can also be used for soldering of some SMD (Suface Mount Device) components that are glued with an SMT (Surface Mount Technology) adhesive to the bottom side of the PCB before passing through the wave soldering process. The wave soldering process comprises three main steps : Fluxing, preheating and soldering. A conveyor transports the PCBs through the machine. The PCBs can be mounted in a frame to avoid adjusting the conveyor width for every different PCB. Fluxing is usually done by means of a spray fluxer but also foam fluxing and jet fluxing are possible. The liquid flux is applied from the bottomside of the PCB on the surface and in the trough holes. The purpose of the flux is to deoxydize the solderable surfaces of the PCB and components and allow the liquid soldering alloy to make an intermetallic connection with those surfaces resulting in a solder joint. The preheating has three main functions. The solvent of the flux needs to be evaporated as it loses its function once its has been applied and it can lead to soldering defects like briding and solder balling when it contacts the solder wave in a liquid state. Water based fluxes in general need more preheating to evaporate than alcohol based fluxes. The second function of the preheating is to limit the thermal shock when the PCB contacts with the liquid solder of the solder wave. This can be important for some SMD components and PCB materials. The third function of the preheating is to promote through hole wetting of the solder. Because of the temperature difference between the PCB board and the liquid solder, the liquid solder will be cooled down when going up the through hole. Thermally heavy boards and components can draw away so much heat from the liquid solder that it is cooled down to the solidification point where it freezes before it gets to the top. This is a typical problem when using Sn(Ag)Cu alloys. A good preheating limits the temperature difference between PCB board and liquid solder and hence reduces the cool down of the liquid solder when going up the through hole. This gives a better chance that the liquid solder will reach the top of the through hole. In a third step the PCB board is passed over a solder wave. A bath filled with a soldering alloy is heated up to soldering temperature. This soldering temperature depends on the used soldering alloy. The liquid alloy is pumped through channels up into a wave former. There are several types of wave formers. A traditional setup is a chip wave combined with a laminar main wave. The chip wave jets solder in the direction of the PCB movement and allows to solder the back side of SMD components that are shielded of wave contact in the laminar wave by the body of the component itself is. The laminar main wave flows to the front but the adjustable back plate is positioned like this that the board will push the wave into a back flow. This will avoid the PCB being dragged through the reaction products of the soldering. A wave former that is gaining popularity is the Wörthmann-wave that combines the function of the chip wave and the main wave in one wave. This wave is more sensitive to the correct setting and bridging. Because of the fact that lead-free soldering alloys need high working temperatures and tend to oxydise quite strongly, a lot of wave soldering processes are done in a nitrogen atmosphere. A new market tendency and the considered by some as the future of soldering is the use of a low melting point alloy like e.g. LMPA-Q. LMPA-Q needs less temperature and reduces oxydation. It also has some cost related benefits like reduced electricity consumption, reduced wear ot of carriers and no need for nitrogen. It also reduces the thermal impact on electronic components and PCB materials.
Key advantages
-
Colophony, also called rosin, is a substance derived from trees that is typically used in soldering fluxes. It can be used in liquid fluxes as well as in gel fluxes. Colophony containing fluxes can be identified by the denomination 'RO' in the IPC classification. Colophony in general provides a good process window in time and temperature but has a number of disadvantages depending on the application that the colophony containing flux is used in. In liquid fluxes for wave and selective soldering, the colophony will give an increased risk on blocking the nozzle of spray and micro jet flux application systems, resulting in more maintenance and higher risk on bad soldering results. The residues of a rosin (=colophony) based flux in the soldering machine and on tools and carriers are quite hard to remove and a solvent based cleaner is usually needed. When the flux with colophony accidentally ends up on the contacts of a connector or contact comb structures like for a remote control or in electro mechanical contactors / relays / switches, it is known to give contact problems and malfunctioning of the electronic unit in the field. Furthermore the residues of the flux that remain on the board can give contact problems with electrical pin testing ( ICT= In Circuit Testing) which can result in delays in production because of false errors. This usually requires cleaning of the PCB and/or the test pins. These expensive test pins are rather fragile and sensitive to be damaged by cleaning. Furthermore the residues of a rosin flux are known not to be compatible with conformal coatings in time. The rosin residue forms a separation layer between the PCB and conformal coating that in time can cause detaching of the conformal coating and also cracking, especially when the electonic unit experiences a lot of temperature cycles (warming up and cooling down). For those reasons fluxes without colophony and more specifically fluxes from the 'OR' classification are generally used for wave and selective soldering. Colophony can also be used in solder wires. Although the colophony provides a good process window in time and temperature, it is very sensitive to discoloration when heated. The discoloration will depend on the type of colophony and the temperature it has seen. As soldering tip temperatures are usually quite high, the colophony in the solder wire will give quite heavy visual residue formation around the solder joints. This will distinguish them from the other solder joints made in reflow, wave and selective soldering. When this is not desirable a cleaning operation needs to be performed. Furthermore the fumes of a colophony containing solder wire are considered hazardous. A fume extraction is mandatory but anyway advisable for any hand soldering operation. Colophony containg wires are still being used quite a lot but colophony free solder wires and more specifically solder wires from the 'RE' classification are gaining importance. Colophony is also used in solder pastes. Beside giving a good process window in time and temperature, it also provides a good stability of the solder paste on the stencil. This will facilitate a stable printing process and hence stable soldering results and defect rates. The discoloration of the rosin in reflow soldering is not so prominent as it is with a solder wire because the temperatures in reflow soldering are lower than in hand soldering. Still the rosin residue has poor compatibility with conformal coating and in time after thermal cycles it might show cracks or detatching of the conformal coating. Although most manufacturers will apply the conformal coating over the solder paste residues, for optimal results it is advisable to clean off the solder paste residues. Giving the benefits of colophony described above, most solder pastes contain colophony.
-
Absolutely halogen free soldering chemistry contains no intentionally added halogens nor halides. The IPC classification allows up to 500ppm of halogens for the lowest 'L0' classification. Soldering fluxes, solder pastes and solder wires from this class are often referred to as 'halogen free'. Absolutely halogen free soldering chemistry goes one step further and does not contain this 'allowed' level of halogens. Specifically in combination with lead-free soldering alloys and on sensitive electronic applications, these low levels of halogens have been reported to cause reliability problems like e.g. too high leakage currents. Halogens are elements from the periodic table like Cl, Br, F and I. They have the physical property that they like to react. This is very interesting from the point of view of soldering chemistry because it is intended to clean off oxides from the surfaces to be soldered. And indeed halogens perform that job very well, even hard to clean surfaces like brass, Zn, Ni,...or heavily oxidized surfaces or degraded I-Sn and OSP (Organic Surface Protection) can be soldered with the aid of halogenated fluxes. Halogens provide a great process window in solderability. The problem however is that the residues and reaction products of halogenated fluxes can be problematic for electronic circuits. They usually have high hygroscopicity and high water solubility and give an increased risk on electro migration and high leakage currents. This means a high risk on malfunctioning of the electronic circuit. Specifically with lead-free soldering alloys there are more reports that even the smallest levels of halogens can be problematic for sensitive electronic applications. Sensitive electronic applications are typically high resistance circuits, measuring circuits, high frequency circuits, sensors,...That's why the tendency is to move away from halogens in soldering chemistry in electronics manufacturing. In general when the solderability of the surfaces to be soldered from component and PCB (Printed Circuit Board) are normal, there is no need for these halogens. Smartly designed absolutely halogen free soldering products will provide a large enough process window to clean the surfaces and get a good soldering result and this in combination with high reliability residues.
-
RoHS stands for Restriction of Hazard Substances. It is a European directive: Directive 2002/95/EC. It restricts the use of some substances that are considered Substances of Very High Concern (SHVC) in electrical and electronic equipment for the territory of the European Union. A listing of these substances can be found below: Please note that this info is subject to change. Always check the website of the European Union for most recent information: https://ec.europa.eu/environment/topics/waste-and-recycling/rohs-directive_nl https://eur-lex.europa.eu/legal-content/EN/TXT/?uri=CELEX:32011L0065 1. Cadmium and cadmium compounds 2. Lead and lead compounds 3. Mercury and mercury compounds(Hg) 4. Hexavalent chromium compounds(Cr) 5. Polychlorinated biphenyls (PCB) 6. Polychlorinated naphthalenes (PCN) 7. Chlorinated paraffins (CP) 8. Other chlorinated organic compounds 9. Polybrominated biphenyls (PBB) 10. Polybrominated diphenylethers (PBDE) 11. Other brominated organic compounds 12. Organic tin compounds (Tributyl tin compounds, Triphenyl tin compounds) 13. Asbestos 14. Azo compounds 15. Formaldehyde 16. Polyvinyl chloride (PVC) and PVC blends 17. Decabrominated diphenyl ester (from 1/7/08) 18. PFOS : EU directive 76/769/EEC (not allowed in a concentration equal to or higher than 0.0005% by mass) 19. Bis(2-ethylhexyl) phthalate (DEHP) 20. Butyl benzyl phthalate (BBP) 21. Dibutyl phthalate (DBP) 22. Diisobutyl phthalate 23. Deca brominated diphenyl ester (in electrical and electronic equipment) Other countries outside of the European Union have introduced their own RoHS legislation, which is to a great extent very similar to the European RoHS.
-
Alcohol based soldering fluxes are liquid fluxes that have alcohol(s) as their principal solvent(s). The majority of liquid fluxes used in electronics manufacturing are still alcohol based. The main reasons are their historical use and hence market share and their in general larger process window compared to water based fluxes. Water based fluxes have numerous advantages to alcohol based fluxes, like lower consumption, no VOC (Volatile Organic Compound)-emmissions, no fire hazard, no need for special transport and storage, lower smell in the production area,...However a lot of electronic manufacturers seem to prefer the larger process window of alcohol based fluxes to the advantages of water based fluxes. Alcohol based fluxes in general are less sensitive to the correct spray fluxer settings to get a good flux application on the surface and in the through holes. Furthermore they are more easily evaporated in the preheating and give less risk on remaining solvent drops creating solder balls, solder splashes or bridging upon wave contact. Another parameter that is complicating the implementation of water based fluxes is that changing a flux in some cases can be a time consuming and costly process. It usually involves homologation testing and approval of end customers. Specifically for EMS (Electronic Manufacturing Servivces = subcontractors) this can be a challenge. Some countries have already implemented legislation that limits the VOC-emission of factory chimneys or imposes taxes on VOC emissions. This appears to be an extra incentive to change to water based fluxes. A recent development forced a lot of manufacturers to look into water based fluxes. The COVID-pandemia in the beginning of 2020, suddenly increased the demand for alcohol based desinfectants to that extent that at a certain moment the availability of alcohols on the market was pretty much non existing. Luckily the industry that produces alcohols was able to ramp up their volumes just in time to avoid electronic manufacturers to fall without fluxes to operate their soldering machines.
-
Increased activity of a soldering product can be needed for surfaces with poor solderability like e.g. brass, unprotected Ni, Oxidised Ag, Cu that was not micro-etched,...or surfaces with degraded solderability like e.g. I-Sn that was stored too long or did see too much heat, Cu-OSP that passed a lead-free reflow profile too long ago,...An indication of the activity of a soldering product is their classification. The most popular and accepted classification for soldering products is the IPC. L0 is the lowest activation class and the standard, it should be suitable for all normal quality conventional surfaces used in electronics assembly. L1 is the lowest activation class but with a halogen content up to 0,5%. These halogens will in most cases already give a better result on many of the previously mentioned surfaces with poor or degraded solderability. The other activation classes are M0 and M1 and H0 and H1. M stands for Medium and H stands for High. 0 stands for up to 500ppm of halogens for both M0 and H0. 1 stands for up to 2% of halogens for the M1 class and for H1 more than 2% of halogens are allowed. Soldering products of the H class are to be treated with care as they can be corrosive and need to be cleaned off, preferrably in a automatised cleaning process.
Documents
-
Available in 1 languages: