WSP 2006
Interflux ® WSP 2006 is an absolutely halide free solder paste with low corrosion water soluble residues after soldering. The residues of WSP 2006 need to be cleaned.
Suitable for
-
Stencil printing is the most used method to apply solder paste on the pads of a PCB (Printed Circuit Board) in the SMT (Surface Mount Technology) assembly line in electronics manufacturing. After stencil printing, SMD (Surface Mount Device) components are placed with their solderable contacts on the solder paste and the PCB is transported through a reflow oven where the components are soldered to the PCB board. Stencil printing can also be used to apply solder paste in trough holes for the Pin in Paste (PiP, intrusive reflow) technology that is meant to solder through hole components in the reflow soldering process . Stencil printing can also be used to apply SMT adhesive (glue) to the PCB board. SMD components are placed with their body on the glue that will be cured in a reflow oven. After that, the SMD components that are glued to the PCB board will be soldered in a wave soldering process. The PCB board is pressed onto a stencil that has apertures where the solder paste needs to be deposited. A volume of solder paste is present on the stencil. A squeegee is lowered onto the stencil with a certain pressure. The squeegee moves over the stencil with a certain printing speed. This will make the solder paste roll into the apertures. The printing speed can be determined by the desired throughput, typical for high volume productions but can be limited by the used solder paste. This speed can vary from 20-150 mm/s. Once the desired speed has been established, a printing pressure will have to be determined for that printing speed. Higher speeds require higher pressures. The correct printing pressure is the minimum pressure needed to get a clean stencil after printing, meaning all excessive solder paste has been removed by the squeegee. The board is moved away vertically from the stencil, the solder paste releases from the stencil and pads of the PCB have solder paste deposits. The goal is to have a well defined printing result where all solder paste has realeased from the stencil and no solderpaste has been pressed between the stencil and the PCB board. The release of the solder paste obviously is more difficult for smaller apertures and thicker stencils. Some design rules say that the ratio of the surface of the aperture to the surface of the sides ('walls') of the aperture is preferrably not smaller than 0,6. The quality of the stencil is a major parameter in good paste release. Rough sides are more likely to adhere solder paste. Different types of stencils exist. The most popular is the stainless steel stencil with laser cut apertures that are smoothened afterwards by a chemical process. Sometimes they are treated with a coating for better paste release. The main reasons for solder paste being pressed in between the stencil and the PCB board is bad sealing between board and stencil or too high printing pressure for the used printing speed. This can lead to solder balling or bridging after reflow. Some printing machines have an automated under stencil cleaning unit that can be programmed to clean the stencil after so many prints. This will facilitate a stable printing result. It is advisable not to use IPA based or water based cleaning liquids in these units as they may affect the solder paste stability. The use of products that have been specifically designed for that purpose is advisable. The stability of the solder paste on the stencil, meaning how well that the solder paste keeps its printing properties over time, is also a parameter for a stable printing process. Some printing machine have integrated AOI (Automated Optical Inspection) that will check the printing result and give an alarm if it deviates from the programmed desired values. This will help to avoid electronic units being produced with solder joints that are not according good standard.
-
Dispensing is a technology used in electronics manufacturing to apply solder paste (or an adhesive) from a syringe to a PCB (Printed Circuit Board). Dispensing is a more flexible way to apply solder paste than standard stencil printing because it allows to selectively apply solder paste with the presence of pre-assembled components on the surface. However dispensing is a much slower process than stencil printing and not suitable for high volume productions. That's why it is mostly used to add extra solder paste in an SMT (Surface Mount Technology) assembly line but also for rework and repair and in prototyping. Dispensing can be done manually or automatically. In rework and repair this is usually done manually with a system that applies pressurised air to the plunger of the syringe and the solder paste is pushed out through a needle. But it can also be done by hand with a manual plunger. In automated processes like in a stand alone dispenser in a SMT assembly line or a in a dispenser built in a stencil printer there are two main systems to push the solder paste out of the syringe: Air pressure and the Archimes screw. Air pressure systems are usually cheaper but the volumetric stability of the solder paste deposits is a bit more difficult to control, especially when the syringe is almost empty and there is a bigger volume of compressed air in combination of less material in the syringe that needs to be moved by this air pressure. Systems with the Archimedes screw are usually more stable and faster. However depending on the solder paste quality, they can be sensitive to some very fine particles of the solder paste that are squashed between the Archimedes screw and the side walls which can block the needle where the solder paste comes out. The smaller and longer the needle, the higher the risk on needle blocking. The needle size is chosen according to the size of the desired solder deposit. The grain size of the solder paste is chosen according to this needle size. In general a type 3 solder paste can be used for needles with an inner diameter bigger than 0,5mm, a type 4 for needles with an inner diameter down to 0,25mm, a type5 for needles with an inner diameter down to 0,15mm. The dispensing performance of a solder paste can vary from one type to another in terms of volumetric stability and sensitivity to needle blocking. If a syringe of solder paste has been stored too long, too warm or too cold, this can also affect the dispensing performance. How much time and temperature will affect the dispensing performance may also vary from one solder paste to another. Solder paste for dispensing can be available in different types of syringes required by the machine where its intended use is for. They can also be available with different types of plungers required by the viscosity of the solder paste to be dispensed. Standard sizes for syringes are 5CC, 10CC and 30CC.
-
Reflow soldering is the most used soldering process in electronics assembly. Mainly SMD (Surface Mount Device) components but also some through hole components are soldered in a reflow oven to a PCB (Printed Circuit Board) by means of a solder paste. The reflow oven is usually a forced convection oven but also vapor phase and IR ovens are possible. The first step of the process is to apply solder paste to the pads of the PCB or in case of through hole components in the through hole. This latter is called Pin in Paste (PiP) or intrusive reflow technology. The main application method is stencil printing but also dispensing and solder paste jetting are possible. Depending on the application method the solder paste will have a different consistency and comes in a different packaging. Solder paste is a mixture of a solder powder and a gel flux. The type of gel flux and the type of powder and in what ratios they are mixed, will determine the consistency of the paste. The solder powder is made of a certain soldering alloy and has a certain grain size (distribution). Finer grains size are used for smaller pitch components and smaller stencil apertures. Dispensing and even more jetting also require finer grain sizes. The gel flux contains substances to deoxydize the surfaces to be soldered. It also contains substances that will determine the consistency and the behavior of the solder paste in the process to a great extent. When stencil printing solder paste, an important parameter is that the solder paste keeps its printing properties during the time it will be on the stencil. This is often referred to as the stability of the solder paste. Solder paste stability is hard to quantify but can be estimated from the stencil life indication in the technical datasheet. After solder paste application SMD components are placed on the solder paste with their solderable connections. In most cases, this is done with a Pick and Place machine. The solder paste needs to have enough adhesion force to keep the components in their place until soldering. A conveyor will transport the PCB through a reflow oven where the PCB board is submitted to a reflow soldering profile. This profile is created by the temperature settings of the different convection zones. They are usually situated as well from the top as from the bottom side. Beside the temperature settings, in some cases also the convection rate of the zones can be programmed to get better or lower heat transfer, or when some high components experience too much force from the convection. It is the goal to get all components to soldering temperatures, which is determined by the used soldering alloy, without damaging or overheating temperature sensitive components. This can be a challenge for units with a large diversity of big and small components or an uneven Cu-distribution in the PCB board. In that perspective a low melting point soldering alloy substantially limits the risk of damaging or predamaging components and PCB boards. The speed of the conveyor will determine the time of the profile and the throughput of the oven. In most cases however the Pick and Place process is limiting the throughput. Not all electronic components are suitable for reflow soldering. Some because of their thermal mass like e.g. big transfos or others because of their thermal sensitivity like e.g. some displays, connectors, relays, fuses,... These components are usually available as a through hole components and soldered in other processes like selective soldering, wave soldering, hand soldering, robot soldering, laser soldering,...
Key advantages
-
Colophony, also called rosin, is a substance derived from trees that is typically used in soldering fluxes. It can be used in liquid fluxes as well as in gel fluxes. Colophony containing fluxes can be identified by the denomination 'RO' in the IPC classification. Colophony in general provides a good process window in time and temperature but has a number of disadvantages depending on the application that the colophony containing flux is used in. In liquid fluxes for wave and selective soldering, the colophony will give an increased risk on blocking the nozzle of spray and micro jet flux application systems, resulting in more maintenance and higher risk on bad soldering results. The residues of a rosin (=colophony) based flux in the soldering machine and on tools and carriers are quite hard to remove and a solvent based cleaner is usually needed. When the flux with colophony accidentally ends up on the contacts of a connector or contact comb structures like for a remote control or in electro mechanical contactors / relays / switches, it is known to give contact problems and malfunctioning of the electronic unit in the field. Furthermore the residues of the flux that remain on the board can give contact problems with electrical pin testing ( ICT= In Circuit Testing) which can result in delays in production because of false errors. This usually requires cleaning of the PCB and/or the test pins. These expensive test pins are rather fragile and sensitive to be damaged by cleaning. Furthermore the residues of a rosin flux are known not to be compatible with conformal coatings in time. The rosin residue forms a separation layer between the PCB and conformal coating that in time can cause detaching of the conformal coating and also cracking, especially when the electonic unit experiences a lot of temperature cycles (warming up and cooling down). For those reasons fluxes without colophony and more specifically fluxes from the 'OR' classification are generally used for wave and selective soldering. Colophony can also be used in solder wires. Although the colophony provides a good process window in time and temperature, it is very sensitive to discoloration when heated. The discoloration will depend on the type of colophony and the temperature it has seen. As soldering tip temperatures are usually quite high, the colophony in the solder wire will give quite heavy visual residue formation around the solder joints. This will distinguish them from the other solder joints made in reflow, wave and selective soldering. When this is not desirable a cleaning operation needs to be performed. Furthermore the fumes of a colophony containing solder wire are considered hazardous. A fume extraction is mandatory but anyway advisable for any hand soldering operation. Colophony containg wires are still being used quite a lot but colophony free solder wires and more specifically solder wires from the 'RE' classification are gaining importance. Colophony is also used in solder pastes. Beside giving a good process window in time and temperature, it also provides a good stability of the solder paste on the stencil. This will facilitate a stable printing process and hence stable soldering results and defect rates. The discoloration of the rosin in reflow soldering is not so prominent as it is with a solder wire because the temperatures in reflow soldering are lower than in hand soldering. Still the rosin residue has poor compatibility with conformal coating and in time after thermal cycles it might show cracks or detatching of the conformal coating. Although most manufacturers will apply the conformal coating over the solder paste residues, for optimal results it is advisable to clean off the solder paste residues. Giving the benefits of colophony described above, most solder pastes contain colophony.
-
Absolutely halogen free soldering chemistry contains no intentionally added halogens nor halides. The IPC classification allows up to 500ppm of halogens for the lowest 'L0' classification. Soldering fluxes, solder pastes and solder wires from this class are often referred to as 'halogen free'. Absolutely halogen free soldering chemistry goes one step further and does not contain this 'allowed' level of halogens. Specifically in combination with lead-free soldering alloys and on sensitive electronic applications, these low levels of halogens have been reported to cause reliability problems like e.g. too high leakage currents. Halogens are elements from the periodic table like Cl, Br, F and I. They have the physical property that they like to react. This is very interesting from the point of view of soldering chemistry because it is intended to clean off oxides from the surfaces to be soldered. And indeed halogens perform that job very well, even hard to clean surfaces like brass, Zn, Ni,...or heavily oxidized surfaces or degraded I-Sn and OSP (Organic Surface Protection) can be soldered with the aid of halogenated fluxes. Halogens provide a great process window in solderability. The problem however is that the residues and reaction products of halogenated fluxes can be problematic for electronic circuits. They usually have high hygroscopicity and high water solubility and give an increased risk on electro migration and high leakage currents. This means a high risk on malfunctioning of the electronic circuit. Specifically with lead-free soldering alloys there are more reports that even the smallest levels of halogens can be problematic for sensitive electronic applications. Sensitive electronic applications are typically high resistance circuits, measuring circuits, high frequency circuits, sensors,...That's why the tendency is to move away from halogens in soldering chemistry in electronics manufacturing. In general when the solderability of the surfaces to be soldered from component and PCB (Printed Circuit Board) are normal, there is no need for these halogens. Smartly designed absolutely halogen free soldering products will provide a large enough process window to clean the surfaces and get a good soldering result and this in combination with high reliability residues.